This question belongs to Metallurgical Engineering Powder Metallurgy
Powder Metallurgy
?

The increase in density and strength of powder compacts for a given strip thickness can be achieve by

Answer & Solution
Correct Answer: Option A
Let's discuss the solution. Join the discussion
Examveda
Question posted by Examveda
Community

Join the Discussion

No comments yet Be the first to discuss this question.
Keep Learning

Related Questions on Powder Metallurgy

Which of the following components can be manufactured by powder metallurgy technique?
A. Cams B. engine disks C. connecting rod D. All of these
Advantages of Casting are: (I) Can create complex part geometries, 3-D shapes (II) Can create both external and internal shapes and large hollow shapes (III) It is a near net shape process for small to large parts (IV) Very good mechanical strength can be obtained for as-cast component
A. III is true, but I, II and IV are not true B. I and IV are true, but II and III are not true C. I, II, III and IV are not true D. I, II and III are true, but IV is not true
During hot isostatic pressing of powder particulates, the pressure and temperatures are
A. in the range of 4 to 30MPa and 500 to 2200°C respectively B. in the range of 40 to 300MPa and 500 to 2200°C respectively C. in the range of 30 to 300MPa and 500 to 2200°C respectively D. in the range of 40 to 300MPa and 50 to 220°C respectively
Density in sintering product is improved by
A. Hot pressing B. Cold pressing C. Coining D. Both B and C