The vacancy concentration during sintering
A. directly proportional to the radius of curvature of the surface
B. equal to the radius of curvature of the surface
C. inversely proportional to the radius of curvature of the surface
D. is independent of the radius of curvature of the surface
Answer: Option C
Which of the following components can be manufactured by powder metallurgy technique?
A. Cams
B. engine disks
C. connecting rod
D. All of these
A. III is true, but I, II and IV are not true
B. I and IV are true, but II and III are not true
C. I, II, III and IV are not true
D. I, II and III are true, but IV is not true
During hot isostatic pressing of powder particulates, the pressure and temperatures are
A. in the range of 4 to 30MPa and 500 to 2200°C respectively
B. in the range of 40 to 300MPa and 500 to 2200°C respectively
C. in the range of 30 to 300MPa and 500 to 2200°C respectively
D. in the range of 40 to 300MPa and 50 to 220°C respectively
Density in sintering product is improved by
A. Hot pressing
B. Cold pressing
C. Coining
D. Both B and C